Heat-sealing barrier paper

ABSTRACT

A paper including a fibrous substrate, a precoat layer including a binder and a mixture of platy filler(s) having a shape factor of at least 15 and of finer filler(s), the size of the particles of which is, for 80% by weight, less than 2 μm (measured according to the ISO 13317-3 SediGraph method) and at least one covering layer applied to the precoat layer, the paper having a water vapour permeability of at most 150 g/m 2 /24 h and preferably of less than 100 g/m 2 /24 h, measured according to the ASTM F1249 standard under so-called tropical conditions of 38° C. and 90% relative humidity.

The present invention relates to the field of packaging papers.

Plastic films are widely used in flexible packagings since they possess water vapour barrier properties necessary for the proper preservation of perishable products or products that have a limited shelf life.

Papers are materials manufactured from fibres, generally cellulosic fibres, therefore of plant origin. They are naturally porous and permeable to gases and cannot, as is, be used for this application.

It is however known to combine papers with other materials (plastics, aluminium, etc.) in order to obtain the barriers necessary for packaging various products and in particular perishable foodstuffs. In this case, the paper substrate is subjected to conversion operations which include, for example, the coating of covering layers made of polymers in dispersion, the extrusion coating of molten polymers or the lamination with plastic or aluminium films. The cost of this paper-based composite having barrier properties has become expensive.

The document U.S. Pat. No. 2,653,870 A describes a process for manufacturing a packaging paper.

Packagings made from barrier papers manufactured on-line are described in application WO 2011/056130. On-line manufacture is understood to mean the manufacture on a single production tool comprising all the elements required for the production of the paper.

However, the barrier level proposed is limited to measurement conditions that are not very restrictive (that are temperate, i.e. 25° C., 75% relative humidity). The barrier level is measured by a water vapour permeability, a weak barrier signifying a high water vapour permeability. It is known in the literature that “tropical” conditions (i.e. 38° C., 90% relative humidity) are much harsher than temperature conditions, and that therefore the barrier measured under temperate conditions is much weaker.

The expression “barrier paper” should be understood to mean a non-porous paper, comprising a fibrous substrate covered with one or more layers, which is sufficiently leaktight to water vapour to withstand the penetration thereof into the packaging, in an amount capable of adversely affecting the preservation of the product or the integrity of the product contained inside.

The invention is interested in particular, but not exclusively, in water vapour barrier papers having a water vapour permeability of at most 150 g/m²/24 h and, preferably, of less than 100 g/m²/24 h, measured according to the ASTM F1249 standard under so-called tropical conditions of 38° C. and 90% relative humidity.

It is advantageous for the barrier paper to also be heat-sealable, in order to allow the formation of the packaging by sealing the paper to itself.

The manufacture of heat-sealable papers involves, for example, laying a covering layer of a heat-sealing polymer on a cellulosic substrate. Such a covering layer has a quite strong tackiness when not dry, and must be able to be dried completely before the paper is wound on itself, to avoid the various turns of the reel sticking to one another.

The application of this covering layer is generally carried out off-line during one or more conversion steps, which makes it possible to have a good coating quality, to benefit from a paper at ambient temperature at the time of the coating which enables the covering layer not to penetrate excessively in the fibrous support, and to be able to adapt the transit time of the reel width in the ovens, to a speed for example of the order of 200 m/min, so that the time of exposure to these heating means is sufficient to completely dry, in depth, the heat-sealing covering layer.

The documents US 2004/121079 A1, WO 2010/052571 A2, US 2014/113080 A1 and WO 2009/112255 A1 disclose papers which are treated off-line.

The papers that offer a barrier to water vapour and that are optionally heat-sealing are generally manufactured in the prior art during conversion operations and conventionally have covering layers of 10 to 30 g/m² when dry which are deposited as one or more thicknesses using various coating means (air knife, reverse gravure, Meyer rod or bar or any other coating method) or by the application of one thick layer using curtain coating.

The off-line conversion of a paper in order to give it water vapour barrier and heat-sealability properties is therefore an extra step in the manufacture of the paper which increases its costs significantly and which limits the development of paper in flexible packaging in favour of plastic film packaging. There is therefore an economic need to improve the productivity of the manufacture of water vapour barrier and heat-sealing papers.

The invention relates to the development of a paper endowed, during its on-line manufacture, with water vapour barrier and heat-sealability properties. This barrier and heat-sealing paper may be used for manufacturing packaging by sealing the paper to itself.

Independently of the way in which the heat-sealing layer is applied, on-line or off-line, the problem is faced of facilitating the deposition of the heat-sealing layer and more generally of any covering layer, heat-sealing or not, applied to a fibrous substrate.

It is generally desirable for the covering layer not to penetrate too deeply into the fibrous substrate, in order to reduce the amount applied to the paper when this layer is polymer-based. Furthermore, a lesser penetration of the covering layer makes it possible to more easily create a barrier film.

The use of a Yankee cylinder is a first solution for reducing the surface porosity.

A second option is the use of a calender before any treatment of the paper.

Another option is to make provision for the presence of a precoat layer in order to reduce the porosity of the paper.

Another option is to combine one or other of the preceding options.

Use may be made, in the formulation of the precoat layer, of certain hydrophobic and highly film-forming latices.

However, the hydrophobic nature of the precoat layer may then pose a problem of wettability during the application of the covering layer, when the latter is aqueous, resulting in a not perfectly homogeneous covering of the precoated fibrous substrate by the covering layer, especially in the case of an on-line process with a high speed of the sheet. In addition, the surface energy of the precoat layer must be sufficiently different from that of the covering layer while complying with the well-known rules of wettability in order to reduce the risk of wetting defects.

Consequently, there remains a need to satisfactorily respond to the problem of the applicability of the covering layer.

The invention meets this need, according to one of its aspects, owing to a paper comprising:

-   -   a fibrous substrate,     -   a precoat layer comprising a binder and a mixture of platy         filler(s) having a shape factor of at least 15 and of filler(s),         notably finer filler(s), the size of the particles of which is,         for 80% by weight, less than 2 μm (measured according to the ISO         13317-3 SediGraph method),     -   at least one covering layer applied to the precoat layer,         the paper having a water vapour permeability of at most 150         g/m²/24 h and preferably of less than 100 g/m²/24 h, measured         according to the ASTM F1249 standard under so-called tropical         conditions of 38° C. and 90% relative humidity.

The presence, in the precoat layer according to this aspect of the invention, of a platy filler having a shape factor of at least 15 and of a finer, in particular non-platy, particulate filler, the size of the particles of which is, for 80% by weight, less than 2 μm (measured according to the ISO 13317-3 SediGraph method), makes it possible to obtain a relatively high barrier level, independently of the hydrophobic or non-hydrophobic nature of the binder.

It is known that platy fillers help to increase the barrier effect owing to the tortuosity that they provide, as taught for example by the document Imerys Technical Guide, Pigments for Paper, May 2008. The presence according to this aspect of the invention of at least one finer, in particular non-platy, particulate filler increases this effect. One tentative explanation is that this filler, by slipping between the platy particles, obstructs the movement of the water molecules even more, in particular around the platy particles. The document WO 2009/117040 A1 discloses platy fillers of clay.

Owing to the barrier effect linked to the particular choice of the fillers present in the precoat layer, a greater freedom exists as regards the nature of the binder used.

It is thus possible to use, in particular, any papermaking binder with no particular barrier property, which makes it possible to obtain the two-fold advantage of a low water vapour permeability for the precoat layer and a good wettability with respect to the covering layer.

The invention makes it possible to have a reinforced barrier effect with the precoat layer, which allows a reduction in the amount of covering layer to be applied or, for an equal amount of covering layer, makes it possible to further increase the barrier level of the paper, which may prove useful for papers that have to be leaktight to water vapour. The reduction in the amount of covering layer needed, owing to the greater barrier power of the precoated paper, facilitates the drying thereof and may make the coating of this layer easier during the on-line manufacture of the paper.

The paper of the invention is preferably produced on a papermaking machine from a fibrous substrate consisting of cellulose fibres and optionally of synthetic fibres.

The cellulose fibres are in general a mixture of short fibres and long fibres.

Additives such as sizing agents, wet strength agents, retention agents or antifoams may be added.

The paper may also contain papermaking fillers such as titanium dioxide, kaolin, calcium carbonate and talc, inter alfa.

The paper is preferably a packaging paper.

Another subject of the invention is a precoated paper suitable for the manufacture of a barrier paper according to the invention as defined above, having a water vapour permeability of at most 150 g/m²/24 h and preferably of less than 100 g/m²/24 h according to the aforementioned standard. The precoated paper may be uncalendered.

Another subject of the invention is a precoating composition for the manufacture of a paper according to the invention, comprising a binder in latex form and a dispersion of a mixture of platy filler(s) having a shape factor of at least 15 and of finer filler(s), the size of the particles of which is, for 80% by weight, less than 2 μm.

Another subject of the invention is a packaging comprising a paper according to the invention, in particular heat-sealed to itself and containing for example a food product.

Another subject of the invention is a process for manufacturing a paper according to the invention, in which the precoating composition as defined above is applied to a fibrous substrate.

Precoat Layer

The precoat layer may be identical to the covering layer or be a pigment layer as defined below.

The precoat layer preferably consists of a mixture of at least one latex and of fillers also sometimes referred to as “pigments”.

The document U.S. Pat. No. 4,018,647 A describes examples of latices.

The latex according to the invention preferably has a Tg (glass transition temperature) measured according to the ASTM E1356 standard of below 25° C. and more preferably of below 10° C. The latex may be selected from the latices of the following chemical natures: styrene-butadiene, styrene-acrylic, acrylic, butyl acrylate, butyl acrylate-styrene-acrylonitrile, etc., and more particularly from styrene-butadiene emulsions.

The amount of latex is preferably at least 15 parts when dry relative to the fillers when dry (100 parts), preferably at least, or even more than, 25 and better still 30 parts per hundred parts of filler.

The fillers are preferably constituted by a mixture of platy filler(s) and finer, in particular non-platy, fillers.

The platy filler(s) are particles in the form of lamellae having a shape factor (ratio between greatest length and thickness) of greater than or equal to 15, more preferably of at least 40 and more preferably still of at least 60.

The precoat layer comprises a binder and a mixture of platy filler(s) having a shape factor of at least 15 and of finer filler(s), notably non-platy filler(s), the size of the particles of which is, for 80% by weight, less than 2 μm (measured according to the ISO 13317-3 SediGraph method). In order to have a mixture of platy filler(s) and of finer filler(s), the size of the particles of which is, for 80% by weight, less than 2 μm, the size of the particles of the platy filler(s) may for example be, for 80% by weight, greater than or equal to 2 μm. According to another example, less than 80% by weight of the platy particles may be less than 2 μm.

In other words, in order to have finer fillers than the platy filler(s), the finer fillers may, according to a first example, have a particles size lower than that of the platy fillers at equivalent weight distribution. According to a second example they can have a weight distribution greater for a same size of particles than that of the platy fillers.

The finer fillers may be selected from all the other pigments used in papermaking, which meet the required size conditions.

The percentage of platy fillers relative to the sum of the fillers may vary from 10% to 90%, preferably from 40% to 90% and more preferably still from 60% to 90%.

The platy fillers may be selected, for example, from kaolin and talc, and mixtures thereof. Between 30% and 80% by weight of platy particles may be of size less than or equal to 2 μm (measured according to the ISO 13317-3 SediGraph method).

The particles of the platy filler(s) are in particular oriented substantially parallel to the surface of the substrate.

The particles of the finer filler(s) may be selected from calcium carbonate, barium sulphate, silica, titanium dioxide and mixtures thereof, etc. They are characterized by a particle size, for 80% by weight, of less than 2 microns, measured according to the ISO 13317-3 SediGraph method.

The finer fillers may also be selected from any other pigment, including kaolin, having a sufficient fineness, in particular a particle size, for 95% by weight, of less than 2 microns, measured according to the ISO 13317-3 SediGraph method.

The binder is preferably selected from the aforementioned latices but other binders or co-binders such as PVOH, starch, CMC, etc. may be used. The binder may comprise a polymer of chemical nature not present in the covering layer.

Covering Layer

The polymers used to obtain the vapour barrier and the heat-sealability are preferably selected from polymers or copolymers based on PVdC (polyvinylidene chloride) or acrylic.

These polymers are applied pure or as a mixture with fillers. The term “pure” is understood to mean without particulate filler. Other products may optionally be added to the dispersion of polymers such as pH control agents, rheological (for example viscosifying) agents, antifoaming agents, wettability agents, etc.

The use of fillers within the covering layer may in particular help to reduce the risk of turns of the reel sticking to one another.

Manufacture

Preferably the covering layer is applied on-line.

The invention makes it possible to obtain good water vapour barrier levels with weights of covering layer that do not exceed 10 g/m² when dry.

Despite the relatively high run speed of the paper imposed by an industrial papermaking machine, of the order for example of 400 m/min, the on-line coating of a composition intended to form the heat-sealing covering layer is possible, on condition that sufficient drying capacity is used to dry the layer before the winding operation. In particular, a relatively low weight of covering layer may facilitate the on-line drying, while providing sufficient barrier properties.

The on-line process makes it possible to increase the productivity by eliminating the handling operations linked to the off-line treatment.

After drying the fibrous substrate, the paper sheet may pass on to a Yankee cylinder in order to improve the surface finish of the sheet and thus the distribution of the first layer.

The sheet may then be treated in a size press or any other equipment of the same type. To avoid too great a penetration of the precoat layer into the fibrous support, a pigment composition may be used beforehand in order to carry out “pore filling”.

This pore-filling composition may contain up to 20 parts when dry, relative to the fillers when dry, of binder such as latex, of styrene-butadiene chemical nature for example, and up to 20 parts when dry, relative to the dry pigments, of co-binders such as starch for example.

This composition preferably contains fillers which have a size generally of less than 2 microns. These fillers may be selected, inter alfa, from kaolins or calcium carbonates or mixtures thereof.

The precoat layer is applied to the support thus treated using any of the coating techniques that may be encountered on papermaking machines. This may in particular be blade coating, rotogravure coating, reverse gravure coating or Meyer rod coating. The precoat layer is deposited with a dry layer weight preferably of between 4 and 12 g/m².

This precoat layer is then dried without contact by one or more infrared ovens and/or one or more hot air ovens.

It is not necessary to have a very high level of smoothness before the application of the covering layer. A Bekk level of 150 seconds is sufficient (measured according to the ISO 5627 standard).

The water vapour barrier and heat-sealing covering layer is applied by coating using any of the coating techniques that may be encountered on papermaking machines. This may for example be blade coating, rotogravure coating, reverse gravure coating or Meyer rod coating. The covering layer is deposited with a dry layer weight preferably of 10 g/m² at most.

This covering layer is then sufficiently dried, to prevent the turns from sticking on the winding reel, using one or more infrared ovens and/or one or more hot air ovens.

Coating may be carried out on the opposite face in order to strengthen the barrier and/or in order to provide other functionalities such as printability, curl correction, etc.

The paper thus produced may optionally be calendered on-line in order to reduce the surface roughness before being wound.

The final basis weight of the paper may be between 45 and 200 g/m2.

The barrier to water vapour measured according to the ASTM F1249 standard at 38° C. and 90% relative humidity is less than 150 g/m²/24 h, and preferably less than 100 g/m²/24 h.

EXAMPLE 1

A fibrous support having a basis weight of 55 g/m² is produced on a papermaking machine operating at 400 m/min. The papermaking machine is equipped with a Yankee cylinder placed before the size press.

The fibrous support is firstly glazed then treated on-line on both its faces by a size press with a pore-filling pigment composition, containing 100 dry parts of kaolin of Amazon Premium type (Cadam), and a mixture of Merifilm 104 starch (Tate&Lyle) and of latex of DL950 type (Dow) in a proportion of 20 dry parts relative to the dry kaolin. The treatment applied is 5 g/m² when dry in total.

It is then coated using a Meyer rod coater with a precoat formulation containing a mixture of platy fillers and of finer particulate fillers and a latex of styrene-butadiene chemical nature of Tg=7° C. (DL950 from Dow Chemical) and dried without contact in an infrared oven then a hot air oven. It is then wound on a reel with no other treatment. The dry weight of the precoat layer applied is 7 g/m² and its formulation is given in the table below:

Material Reference/Nature Suppliers Parts wt % Topsperse GX-N Dispersant COATEX 0.2 0.2 Capim NP Kaolin IMERYS 60.0 45.5 (platy filler) Amazon Premium Kaolin CADAM 40.0 30.4 (finer filler) Bacote 20 Crosslinker QUARRECHIM 1.5 1.1 DL950/Styrene- Styrene-butadiene DOW 30.0 22.8 butadiene latex latex Tg 7° C. Tg 7° C.

The particles size, for 97% by weight, of Amazon Premium, measured according to the IS013317-3 SediGraph method, is less than 2 microns.

The shape factor of the Capim NP particles is 28.

The barrier to water vapour is measured by a Mocon Permatran 3/61 machine according to the ASTM F1249 standard at 38° C. and 90% relative humidity in order to determine the barrier contribution of this precoat layer. It is measured at 334±13 g/m²/24 h. After coating with the covering layer, a barrier is obtained of less than 150 g/m²/24 h.

EXAMPLE 2

The fibrous support is firstly glazed then treated on-line on both its faces by a size press with a pore-filling pigment composition, containing 100 dry parts of kaolin of Amazon Premium type (Cadam), and a mixture of Merifilm 104 starch (Tate&Lyle) and of latex of DL950 type (Dow) in a proportion of 20 dry parts relative to the dry kaolin. The treatment applied is 5 g/m² when dry in total.

It is then coated using a Meyer rod coater with a formulation containing a mixture of platy fillers and of finer particulate fillers and a latex of styrene-butadiene chemical nature of Tg=7° C. (DL950 from Dow Chemical) and dried without contact in an infrared oven then a hot air oven. It is then wound on a reel with no other treatment. The dry weight of the precoat layer applied is 7 g/m² and its formulation is given in the table below:

Material Reference/Nature Suppliers Parts wt % Topsperse GX-N Dispersant COATEX 0.2 0.2 Capim NP Kaolin IMERYS 60.0 45.5 (platy filler) Hydrocarb 95 Calcium carbonate OMYA 40.0 30.4 (finer filler) Bacote 20 Crosslinker QUARRECHIM 1.5 1.1 DL950/Styrene- Styrene-butadiene DOW 30.0 22.8 butadiene latex latex Tg 7° C. Tg 7° C.

The particles size, for 95% by weight, of Hydrocarb 95, measured according to the ISO13317-3 SediGraph method, is less than 2 microns.

The barrier to water vapour is measured by a Mocon Permatran 3/61 machine according to the ASTM F1249 standard at 38° C. and 90% relative humidity in order to determine the barrier contribution of this precoat layer. It is measured at 315±9 g/m²/24 h. After coating with the covering layer, a barrier is obtained of less than 150 g/m²/24 h.

EXAMPLE 3

A paper is produced on-line under the same conditions as in Example 1. But following the deposition of the precoat layer, it is coated on-line with a covering layer consisting of a dispersion of PVdC copolymer (Diofan A297 from Solvay), and dried without contact in an infrared oven then a hot air oven. It is then wound on a reel with no other treatment and no bonding between turns is observed. The dry weight of the covering layer is 6.5 g/m².

The barrier to water vapour is measured by a Mocon Permatran 3/61 machine according to the ASTM F1249 standard at 38° C. and 90% relative humidity. It is measured at 21.0±2.4 g/m²/24 h.

The sealing is then simulated on a laboratory heat-sealing machine by bonding the face covered with the covering layer to itself at 110° C., under 3 bar and for 0.5 second. Next, the force necessary for detaching papers bonded to samples having a width of 15 mm is subsequently measured under an angle of 90 degrees according to the Tappi T540 standard at a speed of 100 mm/min.

A sealing force of 3.5 N/15 mm is obtained.

The invention is not limited to the examples described.

In summary, the invention may have one or more of the following advantageous features:

-   -   the weight of the covering layer does not exceed 10 g/m² when         dry, in particular is strictly less than 10 g/m²,     -   the covering layer comprises or is constituted by a         heat-sealable polymer,     -   the platy filler(s) and the finer filler(s) are of the same         nature,     -   the shape factor of the platy filler particles is at least 40,         more preferably at least 60,     -   the finer filler(s) are non-platy filler(s),     -   the finer filler(s) are platy filler(s),     -   the finer filler(s) have a particle size, for 95% by weight, of         less than 2 microns, measured according to the ISO 13317-3         SediGraph method,     -   the platy filler(s) are mineral filler(s),     -   the finer filler(s) are mineral filler(s),     -   the platy filler(s) are selected from kaolins and talc and         mixtures thereof,     -   the finer filler(s) are selected from kaolins, calcium         carbonate, barium sulphate, silica, titanium dioxide and         mixtures thereof,     -   the finer filler(s) are selected from kaolins,     -   the dry weight of platy filler(s) is between 3% and 58% of the         total dry weight of the precoat layer, the weight of platy         filler(s) preferably being greater than that of the finer         fillers,     -   the dry weight of finer filler(s) is between 3% and 58% of the         total dry weight of the precoat layer,     -   the percentage of platy filler(s), expressed by dry weight,         relative to the sum of the fillers, expressed by dry weight, is         between 10% and 90%, preferably between 40% and 90% and more         preferably still between 60% and 90%,     -   the binder has a glass transition temperature T_(g) below or         equal to 25° C. and more preferably below 10° C.,     -   the binder is selected from latices of styrene-butadiene,         styrene-acrylic, acrylic, butyl acrylate, butyl         acrylate-styrene-acrylonitrile chemical nature, and mixtures         thereof,     -   the binder is selected from latices of styrene-butadiene         chemical nature,     -   the binder is introduced in latex form,     -   the precoat layer comprises at least 15 parts when dry of binder         relative to the weight of fillers when dry (100 parts) and         preferably more than 25, better still 30 parts,     -   the binder comprises a polymer of chemical nature not present in         the covering layer,     -   the covering layer is substantially free of filler,     -   the covering layer is the only layer that covers the precoat         layer,     -   the covering layer comprises one or more polymers selected from         copolymers based on PVdC or on styrene-acrylic and mixtures         thereof,     -   the amount of precoat layer is less than or equal to 12 g/m² by         dry weight,     -   the paper comprises a printing layer on the face of the         substrate opposite the one bearing the precoat layer and the         covering layer,     -   the substrate bears two identical precoat layers on its opposite         faces,     -   the substrate bears two precoat layers of different natures on         its opposite faces,     -   a pore-filling composition is applied to the substrate, and the         precoat layer is applied to the pore-filling composition, the         pore-filling composition being applied preferably by size press         or film press,     -   the basis weight of the fibrous substrate is between 25 and 180         g/m²,     -   the paper is heat-sealable, in particular starting from 90° C.,         when the sealing is carried out by hot clamps, under 3 bar and         for 0.5 s,     -   the water vapour permeability of the barrier paper is less than         100 g/m²/24 h.     -   between 30% and 80% by weight of platy particles are of size         less than or equal to 2um (measured according to the ISO 13317-3         SediGraph method),     -   the paper is heat-sealable, notably to itself, at a         manufacturing rate greater than or equal to 40 bags per minute,         on vertical packaging machines of VFFS (Vertical Form, Fill and         Seal) type, along longitudinal sealing lines of 330 mm per bag,     -   the paper is heat-sealable to itself with a sealing force         greater than or equal to 2 N/15 mm, measured under an angle of         90 degrees according to the Tappi T540 standard at a speed of         100 mm/min, when the sealing is carried out by hot clamps, under         3 bar and for 0.5 s,     -   the temperature of the fibrous substrate during the application         of the precoat layer is greater than or equal to 50° C.,     -   the temperature of the fibrous substrate during the application         of the covering layer is greater than or equal to 70° C.,     -   the final basis weight of the paper is between 45 and 200 g/m².         The expression “comprising a” should be understood as being         synonymous with “comprising at least one”. 

1-37. (canceled)
 38. Paper comprising: a fibrous substrate, a precoat layer comprising a binder and a mixture of platy filler(s) having a shape factor of at least 15 and of finer filler(s), the size of the particles of which is, for 80% by weight, less than 2 μm (measured according to the ISO 13317-3 SediGraph method), at least one covering layer applied to the precoat layer, the paper having a water vapour permeability of at most 150 g/m²/24 h, measured according to the ASTM F1249 standard under so-called tropical conditions of 38° C. and 90% relative humidity.
 39. Paper according to claim 38, the weight of the covering layer not exceeding 10 g/m² when dry.
 40. Paper according to claim 39, the covering layer comprising a heat-sealable polymer, or even being constituted by a heat-sealable polymer.
 41. Paper according to claim 38, the platy filler(s) and the finer filler(s) being of the same nature.
 42. Paper according to claim 38, the shape factor of the platy filler particles being at least
 40. 43. Paper according to claim 38, the finer filler(s) having a particle size, for 95% by weight, of less than 2 microns, measured according to the ISO 13317-3 SediGraph method.
 44. Paper according to claim 38, the platy filler(s) being mineral filler(s).
 45. Paper according to claim 38, the finer filler(s) being mineral filler(s).
 46. Paper according to claim 38, the platy filler(s) being selected from kaolins and talc and mixtures thereof.
 47. Paper according to claim 38, the finer filler(s) being selected from kaolins, calcium carbonate, barium sulphate, silica, titanium dioxide and mixtures thereof.
 48. Paper according to claim 38, the finer filler(s) being selected from kaolins.
 49. Paper according to claim 38, the dry weight of platy filler(s) being between 3% and 58% of the total dry weight of the precoat layer.
 50. Paper according to claim 38, the dry weight of finer filler(s) being between 3% and 58% of the total dry weight of the precoat layer.
 51. Paper according to claim 38, the percentage of platy filler(s), expressed by dry weight, relative to the sum of the fillers, expressed by dry weight, being between 10% and 90%.
 52. Paper according to claim 38, the binder having a glass transition temperature T_(g) below or equal to 25° C.
 53. Paper according to claim 38, the binder being selected from latices of styrene-butadiene, styrene-acrylic, acrylic, butyl acrylate, butyl acrylate-styrene-acrylonitrile chemical nature, and mixtures thereof.
 54. Paper according to claim 38, the binder being selected from latices of styrene-butadiene chemical nature.
 55. Paper according to claim 38, the binder being introduced in latex form.
 56. Paper according to claim 38, comprising in the precoat layer at least 15 parts when dry of binder relative to the weight of fillers when dry (100 parts).
 57. Paper according to claim 38, the binder comprising a polymer of chemical nature not present in the covering layer.
 58. Paper according to claim 38, the covering layer being substantially free of filler.
 59. Paper according to claim 38, the covering layer being the only layer that covers the precoat layer.
 60. Paper according to claim 38, the covering layer comprising one or more polymers selected from copolymers based on PVdC or on styrene-acrylic and mixtures thereof.
 61. Paper according to claim 38, the amount of precoat layer being less than or equal to 12 g/m² by dry weight.
 62. Paper according to claim 38, comprising a printing layer on the face of the substrate opposite the one bearing the precoat layer and the covering layer.
 63. Paper according to claim 38, the substrate bearing two identical precoat layers on its opposite faces.
 64. Paper according to claim 38, the substrate bearing two precoat layers of different natures on its opposite faces.
 65. Paper according to claim 38, a pore-filling composition being applied to the substrate, and the precoat layer being applied to the pore-filling composition.
 66. Paper according to claim 38, the basis weight of the fibrous substrate being between 25 and 180 g/m².
 67. Paper according to claim 38, the paper being heat-sealable.
 68. Paper according to claim 38, the final basis weight of the paper being between 45 and 200 g/m².
 69. Precoated paper suitable for the manufacture of a paper as defined in claim 38, having a water vapour permeability of at most 150 g/m²/24 h according to the ASTM F1249 standard at 38° C. and 90% relative humidity, the precoated paper being uncalendered.
 70. Packaging comprising a paper as defined in claim 38, the paper being heat-sealed to itself, containing a food product.
 71. Process for manufacturing a paper according to claim 38, in which a composition is applied to a fibrous substrate, the composition comprising a binder in latex form and a dispersion of a mixture of platy filler(s) having a shape factor of at least 15 and of finer filler(s), the size of the particles of which is, for 80% by weight, less than 2 μm. 